Influência das variáveis de processamento nas propriedades físicas e mecânicas de cerâmicas à base de subproduto do granito Corumbá

Influence of processing variables on the physical and mechanical properties of ceramics based on Corumbá granite by-product

Influencia de las variables de procesamiento en las propiedades físicas y mecánicas de cerámicas a base de subproducto del granito de Corumbá

Rafaella Cavalcante Regis, Cândido Jorge de Sousa Lobo, Ricardo Emílio Ferreira Quevedo Nogueira, Yara Amorim de Figueiredo, Halisson de Souza Pinheiro

Downloads: 3
Views: 457

Resumo

Este trabalho analisou as propriedades físicas e mecânicas de peças sinterizadas de rejeito do granito Corumbá, oriundo da indústria de rochas ornamentais, produzidas em diferentes cargas de compactação e patamares de sinterização. Os resíduos foram caracterizados por difração de raios X e fluorescência de raios X. Os corpos de prova foram compactados a 20, 40, 60 e 80 kN e sinterizados nas temperaturas de 1130, 1140, 1150 e 1200 °C. As amostras sinterizadas a 1140 °C apresentaram melhor vitrificação e menor perda de forma, sendo então adotadas para realização dos ensaios subsequentes. As peças foram avaliadas quanto à variação volumétrica, porosidade, dureza Rockwell B e compressão diametral. Os resultados obtidos permitiram concluir que não houve variação estatisticamente significativa da dureza e compressão diametral com a variação da pressão de compactação, sendo estas vinculadas exclusivamente à temperatura de sinterização.

Palavras-chave

Rocha ornamental; rejeito; granito Corumbá; cerâmica; propriedades físicas e mecânicas.

Abstract

In this work, sintered samples of Corumbá granite waste, a by-product of the ornamental stone industry, were studied in function of the compaction pressure and sintering temperature. The residues were characterized by X-ray diffraction and X-ray fluorescence. The specimens were compacted at 20, 40, 60 and 80 kN and sintered at 1130, 1140, 1150 and 1200 °C. Samples sintered at 1140 °C showed better vitrification and less loss of shape and were then adopted for carrying out subsequent trials. The samples were evaluated for volumetric change, porosity, Rockwell B hardness and diametral compressive strength. The results showed that there was no statistically significant variation in hardness and diametral compression with the variation in compaction pressure, which are linked exclusively to the sintering temperature effect.

Keywords

Ornamental rock; waste; Corumbá granite; ceramics; physical and mechanical properties.

Resumen

En este trabajo se estudiaron muestras sinterizadas de residuos de granito de Corumbá, subproducto de la industria de la piedra ornamental, en función de la presión de compactación y la temperatura de sinterización. Los residuos se caracterizaron por difracción de rayos X y fluorescencia de rayos X. Las probetas fueron compactadas a 20, 40, 60 y 80 kN y sinterizadas a 1130, 1140, 1150 y 1200 °C. Las muestras sinterizadas a 1140 °C mostraron mejor vitrificación y menor pérdida de forma y fueron luego adoptadas para realizar ensayos posteriores. Las muestras fueron evaluadas por cambio volumétrico, porosidad, dureza Rockwell B y resistencia a la compresión diametral. Los resultados mostraron que no hubo variación estadísticamente significativa en la dureza y resistencia a la compresión diametral con la variación en la presión de compactación, las cuales están ligadas exclusivamente al efecto de la temperatura de sinterización.

Palabras clave

Roca ornamental; residuo; granito Corumbá; cerámica; propiedades físicas y mecánicas.
63d934ffa9539544262b56c3 ci Articles
Links & Downloads

Ceram. Ind.

Share this page
Page Sections